PbO~2纳米粉体的固相合成及其对MnO~2电极材料的改性作用

利用固相氧化反应制备了PbO~2纳米粉体样品，借助XRD，TEM以及循环伏安测试对其性质进行了表征。同时，对反应条件的选择进行了讨论。将所得样品用于改性MnO~2电极，恒流放电测试结果表明，样品掺杂量在1.25%～5.00%间对MnO~2有良好的改性效果，可使改性MnO~2的放电容量得到极大提高。循环伏安测试结果表明，铅的掺入改变了MnO~2的放电机理。在循环扫描过程中，掺杂物与MnO~2均不再以单纯氧化物的形式存在，而是形成了一系列Pb(X)(X=0,Ⅱ)Mn(Y)(Y=Ⅳ，Ⅲ，Ⅱ)复合物的共氧化与共还原，抑制了电化学惰性物质Mn~3O~4的生成和积累，从而有望改善MnO~2的可充性能。纳米PbO~2与常粒径PbO~2与常粒径PbO~2(标记为S)对MnO~2的改性机理类似。但前者对MnO~2的改性效果明显优于后者，当恒流放电至-1.0V时，其放电容量较S样改性MnO~2的放电容量平均高出约30%。     

钠硼解石——水体系溶解和相平衡的研究(英)

Ulexite dissolution in water has been studied in the wide temperature range from 10℃ to 93℃ and two higher temperatures at 120 ℃ and 240 ℃. The analytical results showed that ulexite dissolved congruently from 10 ℃ to 35 ℃ and incongruently from 40 to 68 ℃. The solid component of ulexite, NaCaB₅O₆(OH)₆·5H₂O was dehydrated to form NaCaB₅O₆(OH)₆·H₂O from 50 to 68 ℃ and finally amorphous solid at 68 ℃. This amorphous solid converted into priceite at 71 ℃ and then converted completely to priceite at the boiling point(93℃) of the solution. At both 120 and 240 ℃, the dissolution of ulexite was an incongruent process. Above 120 ℃, ulexite became amorphous solid and then transformed into priceite. In addition to the solid to solid transformation, crystallization of priceite from the solution has also been observed. Based on our experimental results, mechanisms of dissolution, transformation, and crystallization of borate in ulexite-water system are discussed.     

CoTiO3纳米粉体的合成及其对MnO2电极材料的改性作用

采用溶胶-凝胶法制得钙钛矿型CoTiO₃纳米粉体，借助XRD、TEM以及循环伏安测试对其性质进行了表征。不同量的所制样品用于MnO₂电极的物理掺杂，进行了深度恒流放电、循环伏安和充放电测试。结果表明在40%KOH电解质溶液中，样品掺杂量为5%时改性效果较好。纳米CoTiO₃参与了电极反应，抑制了电化学惰性物质Mn₃O₄的生成，从而有效地改善MnO₂的放电性能，放电容量较I.C     

气固吸附等温线的研究进展

综述了近些年来在气固吸附理论研究领域对吸附等温线的研究进展。论述了从早期的BDDT的5种类型吸附等温线，到IUPAC的6种类型吸附等温线，再到基于Ono-kondo晶格模型的Gibbs吸附分类的5种类型吸附等温线．讨论了与各种类型吸附等温线类型相对应的吸附机理，并对滞留回环现象进行了解释和分析。     

Selective Determination of Nanogram γ-Globulin in Human Blood Serum by Resonance Light Scattering of Functionalized Nano-PbS

Functionalized nano-PbS has been prepared and characterized. The functionalized nanoparticles have good dispersibility in water. Reaction of functionalized nano-PbS with γ-globulin (γ-IgG) results an enhanced resonance light scattering (RLS) around 385nm.However, when the content of HSA is lower than 0.5μg/ml^-1 the RLS enhancement is very weak and is nonlinear to concentration of HSA. Based on these results, a new direct quantitative determination method for γ-globulin in blood serum samples without separation is established.Under optimal conditions, the enhanced RLS intensity is in proportion to the γ-IgG concentration in the range 10-500ng/mL. The limit of detection is 2.75ng/mL. This method is proved to be very sensitive, rapid, simple and selective for detection of γ-IgG in blood serum.     

苯乙烯-马来酸酐共聚物的核磁共振分析

利用^1H NMR、^13C NMR及DEPT(无畸变极化转移增强)核磁共振技术研究了苯乙烯-马来酸酐共聚物(SMA)的序列结构和组成，并比较了几种核磁共振实验技术对分析SMA结果的准确性；实验表明^1H NMR是分析组成的简单、快速而有效的方法，DEPT谱进行序列结构计算准确度较高。     

铂铋金属间化合物催化剂的氧还原与抗甲醇氧化性能

采用氩弧熔炼后热处理方法制备了PtBi金属间化合物材料.采用循环伏安法和旋转圆盘电极进行电化学性能测试.通过在0.5 mol•L^－1 H₂SO₄＋0.25 mol•L^－1 CH₃OH溶液中对氧还原的起始电位和电流密度大小比较发现,与光滑铂电极相比,PtBi金属间化合物具有良好的氧还原催化性能和抗甲醇中毒性能.从结构方面分析了PtBi具有抗甲醇中毒性能的原因,认为是PtBi中Pt-Pt的间距大，不利于甲醇的吸附解离. X射线光电子能谱(XPS)结果表明,PtBi材料中Pt的d电子空穴增加,可能是导致PtBi电极表面氧还原电流增大的原因.     

高效液相色谱法测定功能性红曲米粉中的青霉素G钠

采用高效液相色谱法测定了功能性红曲米粉中的青霉素G钠,选用Aichrom Bond-AQ C18(250 mm×4.6 mm i.d.,5μm)色谱柱,V(甲醇)∶V(水)=30∶70为流动相,检测波长为215 nm,流速1 mL/min,结果青霉素G钠在1.0~500 mg/L范围内具有良好的线性关系,r=0.9999;回收率为99.0%~107.5%;检出限为0.2 ng。     

固相微萃取参数选择及其对有机锡分析的影响

固相微萃取是一种新型的、不断发展和完善的样品前处理方法，它与其它技术联用可对多种样品基体中挥发、半挥发性有机化合物进行测定。目前，该技术在毒性金属有机化合物中的应用很少。本文分析参数选择对固相微萃取的影响的同时，还对其在有机锡化合物分析中的应用作了综述。     

6-氨基青霉烷酸在弱碱性阴离子树脂IRA67上的吸附研究

用静态法研究了6-氨基青霉烷酸在弱碱性阴离子交换树脂IRA67上的吸附行为．在溶液pH为8．0，6-APA起始浓度介子3.00mg／m1-20．00mg／ml条件下，测定了25℃时IRA67树脂的静态交换动力学曲线、吸附等温线，并求得了IRA67树脂的平衡速率常数及吸附等温线方程．分别用Langmuir型和Frendlich型方程对IRA67树脂吸附等温线进行线性回归拟合，结果表明，6-APA在IRA67树脂上的吸附更符合Langmuir型吸附．